Cheapest Factory Fe-Based Nanocrystalline Alloy Ribbons - Fe-Based 1K107 Nanocrystalline Ribbon – Malio
Cheapest Factory Fe-Based Nanocrystalline Alloy Ribbons - Fe-Based 1K107 Nanocrystalline Ribbon – Malio Detail:
Description
| Product Name | Fe-Based 1K107 Nanocrystalline Ribbon |
| P/N | MLNR-2132 |
| Width | 5-65mm |
| Thickness | 26-34μm |
| Saturation magnetic induction | 1.25 Bs (T) |
| Coercivity | 1.5 Hc (A/m) |
| Resistivity | 1.20 （μΩ·m ） |
| Magnetostriction coefficient | 1 λs (ppm) |
| Curie temperature | 570 Tc (℃) |
| Crystallization temperature | 500 Tx (℃) |
| Density | 7.2 ρ (g/cm3) |
| Hardness | 880 |
| Thermal expansion coefficient | 7.6 |
Application
● Switching power supply transformers and pulse transformer cores
● Power transformers, precision current transformer cores
● Leakage protection switch transformer iron core
● Filter inductors, energy storage inductors, reactor cores
● EMC common mode and differential mode inductor core
● Saturation reactors, magnetic amplifiers, spike suppressor cores and magnetic beads
Features
Fe-based Nanocrystalline materials are superior to conventional materials and will be the best solution for your application (Figure 1.1).
Figure 1.1 μr versus Bs of different soft magnetic materials
● High saturation magnetic induction (1.25 T) and high magnetic permeability (>80,000) for small volumes and high precision
● Core loss equivalent to 1/5 of iron-based amorphous, with losses as low as 70 W/kg at 100 kHZ, 300 mT
● Saturation magnetostriction coefficient close to 0, with very low operating noise
● Excellent temperature stability, <10% change in material properties over the temperature range -50 to 120 °C
● Excellent frequency characteristics with excellent permeability and low losses over a wide frequency range
● With adjustable magnetic properties, different types of magnetic properties can be obtained by applying different transverse and vertical magnetic fields, or without magnetic field heat treatment, such as low remanence, high rectangular ratio, and high magnetic permeability
Material comparison
| Performance Comparison of Fe-based Nanocrystalline Ribbon with Ferrite Core | ||
|
Basic parameters |
Nanocrystalline Ribbon |
Ferrite Core |
| Saturation magnetic induction Bs (T) |
1.25 |
0.5 |
| Residual magnetic induction Br (T)(20KHz) | ＜0.2 | 0.2 |
| Core losses (20KHz/0.2T)(W/kg) | ＜3.4 | 7.5 |
| Core losses (20KHz/0.5T)(W/kg) | ＜35 | Cannot be used |
| Core losses (50KHz/0.3T)(W/kg) | ＜40 | Cannot be used |
| Magnetic Conductivity (20KHz) (Gs/Oe) | ＞20000 | 2000 |
| Coercive force Hc (A/m) | ＜2.0 | 6 |
| Resistivity (mW-cm) | ＜2 | 4 |
| Saturated magnetostriction coefficient（X10-6） | 400 | 740 |
| Resistivity(mW-cm) | 80 | 106 |
| Curie Temperature | ＞0.7 | - |
Product detail pictures:
Related Product Guide:
Sticking for the principle of "Super Quality, Satisfactory service" ,We have been striving for being a superb small business partner of you for Cheapest Factory Fe-Based Nanocrystalline Alloy Ribbons - Fe-Based 1K107 Nanocrystalline Ribbon – Malio , The product will supply to all over the world, such as: Ireland, Detroit, Amman, Our products are produced with the best raw materials. Every moment, we constantly improve the production programme. In order to ensure better quality and service, we have been focusing on the production process. We have got high praise by partner. We are looking forward to establishing business relationship with you.
By Sally from Durban - 2018.02.08 16:45
Customer service staff and sales man are very patience and they all good at English, product's arrival is also very timely, a good supplier.
By Grace from Las Vegas - 2017.09.28 18:29