Short Lead Time for Led Backlight – Fe-Based 1K107 Nanocrystalline Ribbon – Malio
Short Lead Time for Led Backlight – Fe-Based 1K107 Nanocrystalline Ribbon – Malio Detail:
Description
| Product Name | Fe-Based 1K107 Nanocrystalline Ribbon |
| P/N | MLNR-2132 |
| Width | 5-65mm |
| Thickness | 26-34μm |
| Saturation magnetic induction | 1.25 Bs (T) |
| Coercivity | 1.5 Hc (A/m) |
| Resistivity | 1.20 （μΩ·m ） |
| Magnetostriction coefficient | 1 λs (ppm) |
| Curie temperature | 570 Tc (℃) |
| Crystallization temperature | 500 Tx (℃) |
| Density | 7.2 ρ (g/cm3) |
| Hardness | 880 |
| Thermal expansion coefficient | 7.6 |
Application
● Switching power supply transformers and pulse transformer cores
● Power transformers, precision current transformer cores
● Leakage protection switch transformer iron core
● Filter inductors, energy storage inductors, reactor cores
● EMC common mode and differential mode inductor core
● Saturation reactors, magnetic amplifiers, spike suppressor cores and magnetic beads
Features
Fe-based Nanocrystalline materials are superior to conventional materials and will be the best solution for your application (Figure 1.1).
Figure 1.1 μr versus Bs of different soft magnetic materials
● High saturation magnetic induction (1.25 T) and high magnetic permeability (>80,000) for small volumes and high precision
● Core loss equivalent to 1/5 of iron-based amorphous, with losses as low as 70 W/kg at 100 kHZ, 300 mT
● Saturation magnetostriction coefficient close to 0, with very low operating noise
● Excellent temperature stability, <10% change in material properties over the temperature range -50 to 120 °C
● Excellent frequency characteristics with excellent permeability and low losses over a wide frequency range
● With adjustable magnetic properties, different types of magnetic properties can be obtained by applying different transverse and vertical magnetic fields, or without magnetic field heat treatment, such as low remanence, high rectangular ratio, and high magnetic permeability
Material comparison
| Performance Comparison of Fe-based Nanocrystalline Ribbon with Ferrite Core | ||
|
Basic parameters |
Nanocrystalline Ribbon |
Ferrite Core |
| Saturation magnetic induction Bs (T) |
1.25 |
0.5 |
| Residual magnetic induction Br (T)(20KHz) | ＜0.2 | 0.2 |
| Core losses (20KHz/0.2T)(W/kg) | ＜3.4 | 7.5 |
| Core losses (20KHz/0.5T)(W/kg) | ＜35 | Cannot be used |
| Core losses (50KHz/0.3T)(W/kg) | ＜40 | Cannot be used |
| Magnetic Conductivity (20KHz) (Gs/Oe) | ＞20000 | 2000 |
| Coercive force Hc (A/m) | ＜2.0 | 6 |
| Resistivity (mW-cm) | ＜2 | 4 |
| Saturated magnetostriction coefficient（X10-6） | 400 | 740 |
| Resistivity(mW-cm) | 80 | 106 |
| Curie Temperature | ＞0.7 | - |
Product detail pictures:
Related Product Guide:
Our products are widely recognized and trusted by users and can meet continuously changing economic and social needs for Short Lead Time for Led Backlight – Fe-Based 1K107 Nanocrystalline Ribbon – Malio , The product will supply to all over the world, such as: Borussia Dortmund, Jersey, Auckland, As a way to make use of the resource on the expanding information and facts in international trade, we welcome prospects from everywhere on the web and offline. In spite in the top quality products we offer, effective and satisfying consultation service is supplied by our specialist after-sale service group. Solution lists and detailed parameters and any other info weil be sent to you timely for the inquiries. So please get in touch with us by sending us emails or contact us if you have any concerns about our firm. ou can also get our address info from our web site and come to our enterprise. or a field survey of our solutions. We're confident that we are going to share mutual results and build solid co-operation relations with our companions in this market. We're looking forward to your inquiries.
By Prudence from Curacao - 2017.06.22 12:49
Perfect services, quality products and competitive prices, we have work many times, every time is delighted, wish continue to maintain!
By Lena from Mauritius - 2017.08.16 13:39