Massive Selection for Nanocrystalline Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio

Inquire Now Next Product

Product Detail

Product Tags

Feedback (2)

Which has a positive and progressive attitude to customer's desire, our corporation constantly improves our merchandise quality to satisfy the desires of consumers and further focuses on safety, reliability, environmental demands, and innovation of Amorphous Alloy Ribbon, Solar Inverter Core, Segment Lcd Display Module, Adhering to the business enterprise philosophy of 'customer first, forge ahead', we sincerely welcome consumers from at your home and abroad to cooperate with us provide you greatest services!

Massive Selection for Nanocrystalline Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio Detail:

Description

Product Name	Fe-Based 1K107 Nanocrystalline Ribbon
P/N	MLNR-2132
Width	5-65mm
Thickness	26-34μm
Saturation magnetic induction	1.25 Bs (T)
Coercivity	1.5 Hc (A/m)
Resistivity	1.20 （μΩ·m ）
Magnetostriction coefficient	1 λs (ppm)
Curie temperature	570 Tc (℃)
Crystallization temperature	500 Tx (℃)
Density	7.2 ρ (g/cm3)
Hardness	880
Thermal expansion coefficient	7.6

Application

● Switching power supply transformers and pulse transformer cores

● Power transformers, precision current transformer cores

● Leakage protection switch transformer iron core

● Filter inductors, energy storage inductors, reactor cores

● EMC common mode and differential mode inductor core

● Saturation reactors, magnetic amplifiers, spike suppressor cores and magnetic beads

Features

Fe-based Nanocrystalline materials are superior to conventional materials and will be the best solution for your application (Figure 1.1).

Figure 1.1 μr versus Bs of different soft magnetic materials

● High saturation magnetic induction (1.25 T) and high magnetic permeability (>80,000) for small volumes and high precision

● Core loss equivalent to 1/5 of iron-based amorphous, with losses as low as 70 W/kg at 100 kHZ, 300 mT

● Saturation magnetostriction coefficient close to 0, with very low operating noise

● Excellent temperature stability, <10% change in material properties over the temperature range -50 to 120 °C

● Excellent frequency characteristics with excellent permeability and low losses over a wide frequency range

● With adjustable magnetic properties, different types of magnetic properties can be obtained by applying different transverse and vertical magnetic fields, or without magnetic field heat treatment, such as low remanence, high rectangular ratio, and high magnetic permeability

Material comparison

Performance Comparison of Fe-based Nanocrystalline Ribbon with Ferrite Core
Basic parameters	Nanocrystalline Ribbon	Ferrite Core
Saturation magnetic induction Bs (T)	1.25	0.5
Residual magnetic induction Br (T)(20KHz)	＜0.2	0.2
Core losses (20KHz/0.2T)(W/kg)	＜3.4	7.5
Core losses (20KHz/0.5T)(W/kg)	＜35	Cannot be used
Core losses (50KHz/0.3T)(W/kg)	＜40	Cannot be used
Magnetic Conductivity (20KHz) (Gs/Oe)	＞20000	2000
Coercive force Hc (A/m)	＜2.0	6
Resistivity (mW-cm)	＜2	4
Saturated magnetostriction coefficient（X10^-⁶）	400	740
Resistivity(mW-cm)	80	10⁶
Curie Temperature	＞0.7	-

Product detail pictures:

Related Product Guide:

We know that we only thrive if we will guarantee our combined cost competiveness and high-quality advantageous at the same time for Massive Selection for Nanocrystalline Cut Core - Fe-Based 1K107 Nanocrystalline Ribbon – Malio , The product will supply to all over the world, such as: Casablanca, Paraguay, Japan, After years' creating and developing, with the advantages of trained qualified talents and rich marketing experience, outstanding achievements were gradually made. We get good reputation from the customers due to our good solutions quality and fine after-sale service. We sincerely wish to create a more prosperous and flourishing future together with all the friends home and abroad!

1k107 Strip